S5 PVDF/Kynar Thin Wall Heat Shrink Tube
Features
   Semi-rigid, cross-linked thin wall PVDF   Operating temperature: -55~175
   Excellent abrasion resistance  Shrink temperature: 175 ℃
   Excellent chemical and solvent resistance  Shrink Ratio2:1 
   High flame retardant VW-1   Easy see-through inspection
   High temperature protection              
Dimensions
Reference As supplied(mm) After recovered(mm) Standard length
UPM S5 PVDF ID min. ID max. WT  nom. m
1.2/0.6 1.2 0.6 0.20 200
1.6/0.8 1.6 0.8 0.20 200
2.4/1.2 2.4 1.2 0.23 200
3.2/1.6 3.2 1.6 0.23 200
4.8/2.4 4.8 2.4 0.23 100
6.4/3.2 6.4 3.2 0.28 100
9.5/4.8 9.5 4.8 0.28 1.22
12.7/6.4 12.7 6.4 0.28 1.22
19.0/9.5 19.0 9.5 0.40 1.22
25.4/12.7 25.4 12.7 0.40 1.22
38.1/19.0 38.1 19.0 0.51 1.22
ID=Internal Diameter       WT= wall thickness


 

Technical Data
Property Test method Values
Physical Tensile strength ASTM D638    30 MPa
Breakdown elongation ASTM D638    150%
Aging Tensile strength 180 ℃/168hrs   ≥ 24 MPa
 Breakdown elongation 180 ℃/168hrs   ≥100%
Elasticity   180 ℃/168hrs No cracking
Heat resistance 300 ℃/hr No cracking
Distortion 150℃/hr    ≤ 50%
Incison modulus  --    ≥84.4 MPa
Electrical Volume resistivity ASTM D876   ≥1013 Ω.cm
Dielectric strength  ASTM D2671    15 KV/mm
Chemical  Flammability UL224      VW-1
Copper corrosion 180 ℃/168hrs No corrosion
Copper stability 180 ℃/168hrs Stable 
Typical application
       Designed for applications that requiring 175℃ high temperature protection
Ordering 
      Standard color : Clear, Black 
      Standard packaging on spools and/or 1.22m/pc
      Please specify specification, color, quantity when ordering
Cross reference
Raychem/Tyco : RW-175/ Kynar


 