Introduction
FR-MCA500 using PA6 resin as carrier, content of MCA is above 50%, Advantages: good compatibility with PA6 and PA66 resin, good dispersity, good flame resistance. Environmental protection without halogen, low dosage, no mold corrosion, high effective, low smoke, high cost performance. Flame retardant can reach the level UL94V0.
Index
Item |
FRMCA500 |
FRMCA500H |
Appearance |
White Granular |
Black Granular |
Content wt% |
50 |
50 |
Carrier |
PA6 |
PA6 |
Density g/cm3 |
1.2±0.2 |
1.2±0.2 |
Solubility Index g/min |
230 |
230 |
Decomposition Temp ℃ |
320 |
320 |
Water Content wt% |
≤0.3 |
≤0.3 |
Note
1.FR-MCA500 is suitable for various processing temperature of black nylon 6 and nylon 66, non-discolouring, excellent mechanical properties. Don't catch fire with CTI 600℃, glowing filament 750℃.
2.Suggest adding raw material nylon and drying at 120 ℃ to 4-6 hours; processing temperature is 230-250℃.
3.If you have more detailed requirements for your products, we can provide different design solutions according to your requirements, In order to bring you more convenience and save more cost.
Performance and Advantage
MCA500 mainly used in products which with high flame retardant requirement. Such as, PA bellow, PA conduit, thin-wall products etc., injection and extrusion.
Item |
PA66 Resin |
FR-MCA500 |
FR-MCA500H |
Add 15% |
Add 15% |
||
Tensile Strength MPa |
≥70 |
≥60 |
≥60 |
Izod Impact Strength Notched KJ/m2 |
≥10 |
≥9 |
≥9 |
Tensile Strength MPa |
≥100 |
≥100 |
≥100 |
Density g/cm3 |
1.10-1.15 |
1.2 |
1.2 |
Melting Temp ℃ |
238-248 |
245-250 |
245-250 |
Flame Retardancy UL94 3.2/1.6mm |
Non flame retardant |
V0 |
V0 |
Characteristic |
High brightness,No crystal point |
Black, high level flame retardant |
Packing/Storage
25KG/bag: paper-plastic composite plus polyethylene lining plastic bag packaging, stored in dry and cool place, avoid direct sunlight.